The influence of different etching adhesive systems on flowable resin used as pit and fissure sealant
10.3969/j.issn.1001-3733.2015.06.025
- VernacularTitle:不同酸蚀粘接系统对流动树脂行窝沟封闭的影响
- Author:
Jie LI
;
Jianqi GU
;
Lin WANG
;
Xue YU
;
Qing DONG
- Publication Type:Journal Article
- Keywords:
Pit and fissure sealant;
Flowable resin;
Compressive strength;
Shear bond strengths;
Microleakage
- From:
Journal of Practical Stomatology
2015;(6):848-851
- CountryChina
- Language:Chinese
-
Abstract:
Objective:To evaluate the effects of the flowable resin used as pit and fissure sealant using different etching adhesive systems.Methods:60 caries-free extracted human premolars were randomly divided into 4 groups(n =1 5)and treated by Gluma, NT and 3M-Z350 flowable resin(group A);Clearifil SE Bond adhesive and 3M-Z350 flowable resin(group B),phosphoric acid etching,3M-Z350 flowable resin and phosphoric acid etching(group C)and 3Mconcise sealant(group D)respectively.After pro-cessing the tooth surface the pit and fissue of 1 0 sample in each group were sealed.The microleakage was measured by 1 % methyl-ene blue staining(n =8).The material-enamel interface was observed by SEM(n =2).The shear bond strength of the column-shaped samples with the diameter and the height of 3 mm(n =5)on the mesial or dental surface was examined by a test machine. The sealant cartridges and flowable resin cartridges with the diameter and height of 4 mm were used for the crushing strength exami-nation(n =1 0).Results:There was no significant difference in the microleakage among the 4 groups.SEMobservation showed that the resin tags of group A were long and dense and the resin tags of group B were short and sparse,bubbles and cracks were found on the local site in group A and B.The resin tags of group C were long and thin,but combined with tooth tightly;the resin tags of group D were short and dense;the penetration was poor at the bottom of the fissures in the 4 groups.The shear bond strength of Group A was the highest(P <0.01 ),that of group C was higher than that of group B and D(P <0.05).There was no significantly difference between group B and D(P >0.05).The compressive strength of flowable resin groups was higher than that of fissure seal-ant group(P <0.05).Conclusion:The shear bond strength and compressive strength of all-etching bonding system combined with flowable resin is superior to that of self-etching bonding system combined with flowable resin and the traditional sealant.Using Prime&Bond NT bond after acid etching may improve the shear bonding strength.