Study on antibacterial property of silver loaded titanium dioxide antibacterial coated endotracheal intubation tube
10.3760/cma.j.issn.2095-4352.2014.05.012
- VernacularTitle:载银二氧化钛抗菌涂层气管插管导管的抗菌性能研究
- Author:
Xuhong JIANG
;
Yuan WANG
;
Junyi HUA
;
Bin LYU
- Publication Type:Journal Article
- Keywords:
Silver loaded titanium dioxide;
Endotracheal intubation tube;
Antibacterial coating;
Antibacterial property
- From:Chinese Critical Care Medicine
2014;26(5):343-346
- CountryChina
- Language:Chinese
-
Abstract:
Objective To study the antibacterial property of silver loaded titanium dioxide (TiO2) antibacterial coated endotracheal intubation tube,and to determine the minimum effective antibacterial concentration.Methods Intubation tubes coated with different concentrations of antibacterial agents were prepared with sol gel method.Polyethylene endotracheal intubation tubes were used as substrate,and silver loaded TiO2 was used as the antibacterial agent.According to the different antibacterial concentrations of the antibacterial agent,the tubes were divided into nine groups:10.0％ group,5.0％ group,2.0％ group,1.5％ group,1.0％ group,0.8％ group,0.6％ group,0.2％ group,and conrol group.They were respectively immersed in three standard bacteria suspensions with 1.0 × l05 cfu/mL:Pseudomonas aeruginosa,Staphylococcus aureus,and Escherichia coll Together with standard bacteria liquid group,there were 10 experimental groups.They were kept overnight for 24 hours.10 μL of respective culture medium was smeared on blood agar culture medium.After being cultured overnight in 35 ℃,the number of bacteria colonies was respectively counted.Results In 1.0 × 105 cfu/mL of three standard bacteria liquids with antibacterial agent concentration≥ 1.0％,three bacterial colonies had un-obviously growth rate.Almost the same strong antibacterial effects to achieve sterilizing rates of more than 98％ was shown in each group of the antibacterial coating endotracheal intubation tubes (all P＞0.05).As the antibacterial agent concentration decreased,three bacterial colonies were increasing gradually.Intermediate antibacterial effects were shown in tubes of 0.8％ group,with significant statistic difference as compared with 1.0％ and 0.6％ groups [Pseudomonas aeruginosa:7.300 (4.050,8.350) vs.0.200 (0.050,1.200),9.700 (9.000,10.000); Staphylococcus aureus:4.100 (3.300,4.650) vs.0.000 (0.000,0.150),5.800 (5.350,7.650); Escherichia coli:1.400 (0.750,3.750) vs.0.050 (0.025,0.050),9.500 (8.500,9.800),all P＜0.01].Conclusions Silver loaded TiO2 antibacterial coated endotracheal intubation tube had definite antibacterial properties,which were related to the antibacterial concentration.Strong antibacterial effects were shown when antibacterial concentration was above 1.0％,with bacteria almost completely killed in the immersing liquid.