Poly(butylene succinate)/polypropylenecarbonate biofilms: preparation and performance
10.3969/j.issn.2095-4344.2015.21.014
- VernacularTitle:聚丁二酸丁二醇酯/聚碳酸亚丙酯生物膜的制备及相关性能评价
- Author:
Yao MA
;
Shunli CHU
;
Yue SUN
;
Shanshan MA
;
Xue LI
;
Tianshou ZHANG
;
Yanmin ZHOU
- Publication Type:Journal Article
- From:
Chinese Journal of Tissue Engineering Research
2015;19(21):3355-3360
- CountryChina
- Language:Chinese
-
Abstract:
BACKGROUND:Poly(butylene succinate) (PBS) and polypropylenecarbonate (PPC) are new medical materials developed in recent years, characterized as good biocompatibility, biodegradability and the low price. OBJECTIVE:To prepare the PBS/PPC biofilm by electrostatic spinning method and evaluate its physical and chemical properties, degradation performance and effect on cel proliferationin vitro. METHODS:The PBS/PPC biofilm was prepared using electrostatic spinning method: 0.9 g PBS and 0.9 g PPC were dissolved in 10 mL of trichloromethane at room temperature and stirred magneticaly until they were fulydissolved. Then, the spinning solution was added into a spinning tube with a distance of about 15 cm and at a voltage of 18 kV. The surface morphology was observed by scanning electron microscopy. The intensity, contact angle and water absorption, pH value and weight loss in the process ofin vitro degradation were measured. MG63 cels were co-cultured with the biofilm for 7 days and cel proliferation was detected by cel counting kit-8. RESULTS AND CONCLUSION: The PBS/PPC biofilm showed a porous structure with interconnected pores. The fiber diameter was about 0.88 μm, the average aperture was about 5.68 μm, the porosity was 78.3%, the fracture intensity was 2.31 MPa, the elongation rate at break was 23.48%, the average value of contact angle was 87°, and the water absorption rate was 68.54%. During the biofilm degradation, the pH value decreased gradualy andreduced to 6.76 at 12 weeks; meanwhile, the biofilm degraded equaly and gradualy, and the weight loss rate was 6.04% at the end of the 12th week. The results of cel counting kit-8 showed that the PBS/PPC biofilm could promote cel proliferation. Overal, the PBS/PPC biofilm has good physical and chemical properties, good space-making feature, wettability and degradability, which can provide sufficient time for bone tissue regeneration.