The effects of thermocycling on the tensile bond strength of silicone denture liner incorporated with silver-nano-particles
- VernacularTitle:冷热循环对载银软衬材料拉伸强度的影响
- Author:
Meng WANG
;
Huaiqin ZHANG
;
Xiaochen LU
- Publication Type:Journal Article
- Keywords:
Nano-silver;
Soft denture liner;
Thermocycling;
Tensile bond strength
- From:
Journal of Practical Stomatology
2014;(5):709-711
- CountryChina
- Language:Chinese
-
Abstract:
16 standered acrylic resin blocks with silicone resilient denture liner(10 mm ×8 mm ×3 mm)incorporated with nano-silver par-ticles at 5% (m/m,by dry wet)in-between were prepared.8 blocks were immersed in distilled water for 24 h at 37 ℃ as the controls (group 1).Another 8 were thermocycled for 4 000 cycles(group 2).16 acrylic resin bars were thermal cycled for 4 000 cycles.Then they were processed exactly as the control group (group 3).Tensile bond strength of the specimens was measured by a universal testing machine. The bond strength values(MPa)of group 1,2 and 3 were 2.683 ±0.435,2.179 ±0.633 and 1.460 ±0.566 respectively(group 1 vs 2,P>0.05;group 3 vs 1 or 2,P<0.05).The failure mode of the blocks in group 1 and 2 was mainly cohesive failure,in group 3 adhesion fail-ure.