Preparation of tissue-engineered esophageal scaffolds using electrospinning technology
10.3969/j.issn.2095-4344.2014.30.003
- VernacularTitle:电纺丝技术制备组织工程食管仿生支架
- Author:
Xuechan YU
;
Qiuxia SHEN
;
Zhenzhen LU
;
Chen ZHANG
;
Ling DENG
;
Pin HU
;
Yabin ZHU
- Publication Type:Journal Article
- Keywords:
nanofibers;
gelatin;
silk
- From:
Chinese Journal of Tissue Engineering Research
2014;(30):4771-4776
- CountryChina
- Language:Chinese
-
Abstract:
BACKGROUND:We have found that oriented fibers can guide the alignment of smooth muscle cells in our previous experiments. Thus, we designed the experiment to prepare wel aligned polymeric fibers using electrospinning technology, aiming at guiding the growth of esophageal smooth muscle cells to maintain cellmorphology and biological function. OBJECTIVE:Using electrospinning technology, to fabricate isotropic and directed nano-fibrous scaffolds made of polycaprolacton, gelatin and silk fibroin. METHODS:Polycaprolacton/silk fibroin fibers at a ratio of 4:1 were prepared with proper parameters, including solution concentration, voltage and injection speed, under the self-made spinning system. The polycaprolacton/gelatin sheets with mass ratio of 2:1, 1:1 and 1:2, respectively, were also fabricated under suitable process parameters. Using the rol er col ector instead of the metal plate, polycaprolacton/gelatin nano-fibrous scaffold with good alignment of fibers was manufactured. RESULTS AND CONCLUSION:The isotropic polycaprolacton/silk fibroin scaffold with fiber diameter of (535.9±126.7) nm was prepared under conditions of solution concentration (0.08 g/mL), injection speed (1.6 mL/h) and voltage (22.5 kV), and these fibers were uniform with no beads. The isotropic polycaprolacton/gelatin scaffold with fiber diameter of (257.9±117.8) nm was prepared under conditions of solution concentration (0.10 g/mL), injection speed (0.8 mL/h) and voltage (22.5 kV). Using the rol er col ector instead of the previous metal plate, polycaprolacton/gelatin (w:w, 1:2) nano-fibrous scaffold with good alignment of fibers was manufactured. The process parameters were 3 000 r/min of rol ing speed, 0.8 mL/h of injection speed and 15 kV of voltage.