In vitro evaluation of the bond strength between various ceramics and cobalt-chromium alloy fabricated by selective laser sintering.
- Author:
Eun Jeong BAE
1
;
Hae Young KIM
;
Woong Chul KIM
;
Ji Hwan KIM
Author Information
- Publication Type:In Vitro ; Original Article
- Keywords: Rapid prototyping; Selective Laser Sintering; Dental technique; Bond strength; Coefficient of thermal expansion
- MeSH: Alloys*; Ceramics*; Fires; Powders
- From:The Journal of Advanced Prosthodontics 2015;7(4):312-316
- CountryRepublic of Korea
- Language:English
- Abstract: PURPOSE: This study aimed to present the clinical applicability of restorations fabricated by a new method, by comparing the bond strength of between ceramic powder with different coefficient of thermal expansion and alloys fabricated by Selective laser sintering (SLS). MATERIALS AND METHODS: Fifty Co-Cr alloy specimens (25.0 x 3.0 x 0.5 mm) were prepared by SLS and fired with the ceramic (8.0 x 3.0 x 0.5 mm) (ISO 9693:1999). For comparison, ceramics with different coefficient of thermal expansion were used. The bond strength was measured by three-point bending testing and surfaces were observed with FE-SEM. Results were analyzed with a one-way ANOVA (alpha=.05). RESULTS: The mean values of Duceram Kiss (61.18 +/- 6.86 MPa), Vita VM13 (60.30 +/- 7.14 MPa), Ceramco 3 (58.87 +/- 5.33 MPa), Noritake EX-3 (55.86 +/- 7.53 MPa), and Vintage MP (55.15 +/- 7.53 MPa) were found. No significant difference was observed between the bond strengths of the various metal-ceramics. The surfaces of the specimens possessed minute gaps between the additive manufactured layers. CONCLUSION: All the five powders have bond strengths higher than the required 25 MPa minimum (ISO 9693); therefore, various powders can be applied to metal structures fabricated by SLS.