In vivo study of five porous bioceramic scaffolds implanted in animal muscle
10.3760/cma.j.issn.0253-2352.2012.05.023
- VernacularTitle:五种多孔生物陶瓷支架的肌肉植入实验研究
- Author:
Songfeng XU
;
Zhen WANG
;
Xiuchun YU
;
Lin WANG
;
Kaili LIN
;
Jiang CHANG
- Publication Type:Journal Article
- Keywords:
Silicates;
Bone morphogenetic proteins;
Rabbits
- From:
Chinese Journal of Orthopaedics
2012;32(5):507-514
- CountryChina
- Language:Chinese
-
Abstract:
ObjectiveTo investigate the in vivo biological performance of 5 porous bioceramic scaffolds,which were bioglass,β-tricalcium phosphate (β-TCP),hydroxyapatite (HA),β-calcium silicate (β-CS) and α-CS,implanted in rabbit dorsal muscle.MethodsThe 5 porous bioceramic scaffolds were fabricated by adding pore-forming materials and sintering,and then were investigated by X-ray diffraction,porosity mensuration and biomechanics test.The scaffolds were implanted into rabbit dorsal muscle for 4,8,12,16 weeks,respectively.The samples were analyzed by X-ray,Micro-CT,histological analysis,scanning electron microscope (SEM) and energy dispersive spectrometer (EDS).The expression of bone morphogenetic protein(BMP-2) and BMP-7 in the muscle in touch with bioceramic scaffolds were also investigated by polymerase chain reaction(PCR).ResultsThe characteristic analysis of 5 scaffolds showed that the sequence of compressive strength was bioglass＞α-CS＞β-CS＞β-TCP＞HA,the sequence of elasticity modulus was α-CS＜β-TCP＜HA＜β-CS＜bioglass.It was confirmed by X-ray,Micro-CT and histological analysis that the sequence of biodegradability was β-CS＞α-CS＞β-TCP＞bioglass＞HA.The histological observation showed no new bone formation in five scaffolds.A Ca-P layer was formed in the surface of bioglass,α-CS and β-CS,which suggested their in vivo bioactivity.After 16 weeks,the expression of BMP-2 and BMP-7 was found only in β-CS.Conclusion The porous calcium silicate scaffold,which was promising for bone tissue engineering,was with good in vivo bioactivity and biodegradability,without in vivo osteoinductivity.