Biopolymer poly hydroxybutyrate-hydroxyvalerate membrane
10.3969/j.issn.1673-8225.2011.42.007
- VernacularTitle:可降解聚羟基丁酸酯-羟基戊酸酯的共聚物膜
- Author:
Jianhong CHEN
;
Qian TANG
;
Jian WU
;
Huanyou LIANG
- Publication Type:Journal Article
- From:
Chinese Journal of Tissue Engineering Research
2011;15(42):7817-7821
- CountryChina
- Language:Chinese
-
Abstract:
BACKGROUND: Poly hydroxybutyrate-hydroxyvalerate (PHBV) has been used to construct bioprosthetic heart valve. It remains unclear whether it can be used as membrane for guided bone regeneration. OBJECTIVE: To investigate the biocompatibility of PHBV membrane and evaluate its efficiency of promoting bone regeneration in vivo. METHODS: Effects of 100%, 75%, 50%, 25% PHBV extract solution on relative growth rate of dog bone marrow mesenchymal stem cells were measured by MTT method and cytotoxicity of the biomaterials was evaluated. Bone defects were made on distal bilateral tibias and treated with PHBV membrane; the proximal bilateral tibias undergoing reduction of periosteal flap and were used as control. RESULTS AND CONCLUSION: The toxicity gradation of PHBV membranes was grade 0-1. That is, they were not toxic to growth and proliferation of bone marrow mesenchymal stem cells. New bone regeneration was observed in the defects covered with PHBV membranes at week 2 post-surgery. The defects covered with PHBV membranes were filled with mature bone at week 12 post-surgery. The bone repair in experimental groups was earlier and better than that in control groups. Results demonstrated that PHBV membrane, which has no cytotoxicity to mesenchymal stem cells in a wide range of extract concentration, could be a promising biopolymer membrane for guided bone regeneration.