Biological healing mechanism of magnetic porous Ca3 (PO4) 2: an experimental study

VernacularTitle:磁性生物陶瓷生物愈合机制的实验研究
Author: Zhaohui LOU ; Xianjie DONG ; Anmin CHEN ; Zhengcai XIA ; Shuzhen SUN ; Tao CHENG
Publication Type:Journal Article
Keywords: Fracture healing; Ceramics
From: Chinese Journal of Trauma 2011;27(7):659-662
CountryChina
Language:Chinese
Abstract: Objective To study the causes and theoretical basis for good bone healing ability of magnetic Porous Ca3 (PO4) 2 ( MPTCP). Methods Seven MPTCP specimens with size of 2 cm × 1 cm × 0.5 cm were placed in the material physical system for detecting 42 times and the mean detection value was used to measure the MPTCP curve. The attachment 16451B of impedance spectrometer HP RLC was employed to measure dielectric spectroscopy and dielectric spectroscopy of MPTCP. Four-wire method was used to measure the impedance of MPTCP. Results The magnetic intensity changed rapidly when magnetic field was in a range of-10,000-10,000 Oe. The peak of dielectric spectroscopy and impedance of magnetic bioceramics was in the range of 103-104 Hz. When the external electromagnetic wave of frequency was ≤ 1 000 Hz, electrical impedance of MPTCP was large;while when the electromagnetic wave frequency was≥1 000 Hz, the impedance was relatively small and stable. Conclusion The environmental magnetic fields may change the magnetic and electric behavior of MPTCP and promote the biological healing, which may be the cause for the good bone healing ability of MPTCP.