Repairing large area osteochondral defects using Mosaicplasty modified by autologous bone mesenchymal stem cells combined with alginate calcium gel
10.3969/j.issn.1673-8225.2009.47.010
- VernacularTitle:自体骨髓基质干细胞及可注射藻酸钙凝胶联合Mosaicplasly技术修复山羊膝关节股骨头大面积缺损
- Author:
Chengyu Lü
;
Haining ZHANG
;
Yingzhen WANG
;
Changyao WANG
;
Hao XU
- Publication Type:Journal Article
- From:
Chinese Journal of Tissue Engineering Research
2009;13(47):9253-9256
- CountryChina
- Language:Chinese
-
Abstract:
BACKGROUND: The existed repair method for cartilage defects has shortcomings of insufficient repairing tissue numbers, poor biomechanical properties, as well as donor site complication. Thus it is deficient to repair large-sized osteochondral defects using one method.OBJECTIVE: To investigate the therapeutic effect of tissue engineering modified Mosaicplasty on repairing large-sized osteochondral defects.DESIGN, TIME AND SETTING: A randomized controlled animal experiment was performed at the Center Laboratory of Qingdao University Medical College from January to September 2009.MATERIALS: The hircine bone mesenchymal stem cells (BMSCs) were in vitro cultured, and resuspended with algin solution to obtain BMSCs-calcium alginate gel.METHODS: Totally 12 goats were prepared for osteochondral defects models and were divided into 3 groups.BMSCs-Mosaicplasty group, BMSCs compound with injectable alginate calcium gel was then applied to fill the "dead space" after Mosaicplasty. In the Mosaicplasty group, the defects were repaired by Mosaicplasty. There was no treatment in the control group.From 4 to 16 weeks postoperatively, the animals were sacrificed and the in gross and under electromicroscopy.MAIN OUTCOME MEASURES: ①Gross observation: the joint was exposed to observe the repair effect at weeks 4, 8,16 after operation. ②Histological examination: specimens were harvested at 16 weeks after operation and observed by haematoxylin-eosin staining, toluidine blue staining under light microscopy. ③Transmission electron microscope was used at 16 weeks after operation.RESULTS: The transplanted subchondral bone and superficial cartilage was integrated hardly with each other or with recipient sites in tissue engineering modified Mosaicplasty groups at 16 weeks after operation. The quality and appearance of the transplanted and regenerated cartilage was similar to normal hyaline cartilage. Under microscopy, the regenerated cartilage was integrated with neighbor tightly in regular arrange. ECM distributed evenly and deeply stained by alcian blue. There was no obviously repaired in the control group.CONCLUSION: Tissue engineering can ameliorate the outcome of Mosaicplasty to repair the osteochondral defects.