Effect of titanium surface microgrooves and thermal oxidation on in vitro osteoblast responses.
10.4047/jkap.2015.53.3.198
- Author:
Jin Ho SEO
1
;
Richard LEESUNGBOK
;
Su Jin AHN
;
Su Jung PARK
;
Myung Hyun LEE
;
Suk Won LEE
Author Information
1. Department of Biomaterials & Prosthodontics, Kyung Hee University Hospital at Gangdong, School of Dentistry, Kyung Hee University, Seoul, Republic of Korea. ysprosth@hanmail.net
- Publication Type:In Vitro ; Original Article
- Keywords:
Titanium;
Microgrooves;
Thermal oxidation;
Osteoblastic differentiation
- MeSH:
Alkaline Phosphatase;
Analysis of Variance;
Bromodeoxyuridine;
Calcium;
Cell Adhesion;
Humans;
Microscopy;
Osseointegration;
Osteoblasts*;
Periodontal Ligament;
Titanium*
- From:The Journal of Korean Academy of Prosthodontics
2015;53(3):198-206
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
PURPOSE: We aimed to investigate the effect of combined various microgrooves and thermal oxidation on the titanium (Ti) and to evaluate various in vitro responses of human periodontal ligament cells (PLCs). MATERIALS AND METHODS: Grade II titanium disks were fabricated. Microgrooves were applied on titanium discs to have 0/0 microm, 15/3.5 microm, 30/10 microm, and 60/10 microm of respective width/depth by photolithography. Thermal oxidation was performed on the microgrooves of Ti substrata for 3 h at 700degrees C in air. The experiments were divided into 3 groups: control group (ST), thermal oxidation group (ST/TO), and combined microgrooves and thermal oxidation group (Gr15-TO, Gr30-TO, Gr60-TO). Surface characterization was performed by field-emission scanning microscopy. Cell adhesion, osteoblastic differentiation, and mineralization were analyzed using the bromodeoxyurdine (BrdU), Alkaline phosphatase (ALP) activity, and extracellular calcium deposition assays, respectively. Statistical analysis was performed using the oneway analysis of variance and Pearson's bivariate correlation analysis (SPSS Version 17.0). RESULTS: In general, the combined microgrooves and thermal oxidation group (Gr15-TO, Gr30-TO, Gr60-TO) showed significantly higher levels compared with the control (ST) or thermal oxidation (ST-TO) groups in the BrdU expression, ALP activity, and extracellular calcium deposition. Gr60-TO group induced highest levels of cell adhesion and osteoblastic differentiation. CONCLUSION: Within the limitation of this study, we conclude that the Ti surface treatment using combined microgrooves and thermal oxidation is highly effective in inducing the cell adhesion andosteoblastic differentiation. The propose surface is also expected to be effective in inducing rapid and strong osseointegration of Ti oral implants.