The study on strengthening of fluorophlogopite-based dental machinable ceramic.
- Author:
Qiang FU
1
;
Feng QIN
;
Yong LI
;
Xin-ping FAN
;
Yun-feng ZHAO
;
Yun SHEN
Author Information
- Publication Type:Journal Article
- MeSH: Aluminum Silicates; chemistry; Dental Materials; Dental Porcelain; chemistry; Materials Testing; Tensile Strength
- From: Chinese Journal of Stomatology 2005;40(1):27-29
- CountryChina
- Language:Chinese
-
Abstract:
OBJECTIVETo study the strengthening of fluorophlogopite-based dental machinable ceramic through developing a new type of calcium-mica-based ceramic.
METHODSBased on the analysis of the crystal structure of the fluorophlogopite ceramic of Dicor MGC, the structure of a new type of calcium-mica-based ceramic was designed and the corresponding composition of the new material was experimented. And the new glass-ceramic was obtained through the treatment of glass preparation and nucleation. Then crystal content of the glass ceramic was analyzed by X-ray diffraction analysis (XRD) and the 3-point bending strength of the new ceramic was recorded.
RESULTSA new type of calcium-mica-based glass ceramic was developed and had the 3-point bending strength of (210.2 +/- 14.7) MPa. Compared with the strength of fluorophlogopite-based dental machinable ceramic, such as Dicor MGC, which was reported in the range of 150 approximately 180 MPa within inclusive studies, the higher strength of the new ceramic was recorded.
CONCLUSIONSThe fluorophlogopite-based dental machinable ceramic could be reinforced through internal strengthening.