Research on ultrasonic permeability of low intensity pulsed ultrasound through PTFE membrane and Bio-Gide collagen membrane.
- Author:
Zhaowu CHAI
;
Chunliang ZHAO
;
Jinlin SONG
;
Feng DENG
;
Ji YANG
;
Xiang GAO
;
Minyi LIU
- Publication Type:Journal Article
- MeSH:
Biocompatible Materials;
Collagen;
chemistry;
Membranes, Artificial;
Permeability;
Polytetrafluoroethylene;
chemistry;
Ultrasonics
- From:
Journal of Biomedical Engineering
2013;30(6):1171-1175
- CountryChina
- Language:Chinese
-
Abstract:
The aim of the present study was to detect the transmission rate of ultrasonic low intensity pulsed ultrasound (LIPUS) through polytetrafluoroethylene (PTFE) membrane (Thickness: 0.01 mm) and Bio-Gide collagen membrane, and to provide the basis for the barrier membrane selection on the study of LIPUS combined with guided tissue regeneration (GTR). The ultrasonic (LIPUS, frequency 1.5 MHz, pulse width 200 micros, repetition rate 1.0 kHz) transmission coefficient of the two kinds of barrier membrane were detected respectively through setting ten groups from 10 to 100mW/cm2 every other 10 mW/cm2. We found in the study that the ultrasonic transmission coefficient through 0.01 mm PTFE membrane was 78.1% to 92.%, and the ultrasonic transmission coefficient through Bio-Gide collagen membrane was 43.9% to 55.8%. The ultrasonic transmission coefficient through PTFE membrane was obviously higher than that through Bio-Gide collagen membrane. The transmission coefficient of the same barrier membrane of the ultrasonic ion was statistically different under different powers (P < 0.05). The results showed that the ultrasonic transmittance rates through both the 0.01 mm PTFE membrane and Bio-Gide collagen membrane were relatively high. We should select barrier membranes based on different experimental needs, and exercise ultrasonic transmission coefficient experiments to ensure effective power.