A study on alpha-tricalcium phosphate bone cement carbon fiber-reinforced.
- Author:
Wenjin WU
1
;
Weizhong YANG
;
Dali ZHOU
;
Jiang MA
;
Bin XIAO
Author Information
1. College of Material Science and Engineering, Sichuan University Chengdu 610064, China.
- Publication Type:Journal Article
- MeSH:
Bone Cements;
chemistry;
Calcium Phosphates;
chemistry;
Carbon;
chemistry;
Durapatite;
chemistry;
Materials Testing
- From:
Journal of Biomedical Engineering
2006;23(3):569-572
- CountryChina
- Language:Chinese
-
Abstract:
In order to improve the mechanical properties of alpha-tricalcium phosphate (alpha-TCP), we prepared surface-modified carbon fibers (CF) reinforced alpha-TCP composite bone cement. Bone cement was soaked in Ringer's body solution to test its capacity of fast formation of hydroxyapatite crystals and self-solidification. Scan electronic microscope (SEM) observation and compressive strength measurement were taken to analyze the mechanical properties and the micro- morphological structure of CF reinforced alpha-TCP bone cement. The results showed that the bone cement was transferred into hydroxyapatite plates after being soaked in Ringer's simulated body fluid for 5 days. Suitable amount of carbon fibers could well spread in and bond with the matrix of the bone cement. The mechanical properties of the bone cement have been improved by CF reinforcing; the compressive strength reaches 46.7 MPa when the amount of carbon fibers is 0.5% in weight percent, which is 22% higher than that of the non-reinforced alpha-TCP bone cement.