Effect of Ti bonder on the bond strength between porcelain and titanium
10.3760/cma.j.issn.1002-0098.2009.12.014
- VernacularTitle:粘接瓷对纯钛与低熔瓷粉结合强度的影响
- Author:
Hai YAO
1
;
Xiao-Ping LUO
Author Information
1. 南京大学口腔医学院
- Keywords:
Titanium;
Dental porcelain;
Shear strength
- From:
Chinese Journal of Stomatology
2009;44(12):756-758
- CountryChina
- Language:Chinese
-
Abstract:
Objective To investigate the influence of GC Initial Ti Bonder on bend strength between Vita Titankeramik porcelain and titanium.Methods Forty titanium samples were prepared and randomly assigned to 4 groups with 10 samples in each group.Samples in each group were subjected to one of the following surface treatments,burnishing(Group B),sandblasting(Group S),firing GC Initial Ti Bonder after burnishing(Group BG) and firing GC Initial Ti Bonder after sandblasting(Group SG).Vita Titankeramik porcelain were fired on the surface of each sample in the middle.Three-point bending tests were conducted on each sample according to the ISO 9693.The fracture patterns of all specimens were recorded using zoom stereo microscope (ZSM) and the fracture surfaces were observed under scanningelectron microscope (SEM).Results With fired GC Initial Ti Bonder,the bend strength of Vita Titankeramik porcelain to titanium in Group BG and Group SG were (32.72±4.46) and (34.25±6.52) MPa respectively,which reach the ISO 9693 standard for clinical use and were significantly higher than those in Group B [(20.70±3.15) MPa]and Group S [(23.92±5.02) MPa].Conclusions GC Initial Ti Bonder can significantly improve bend strength between Vita Titankeramik porcelain and titanium.