The change of bacterial adhesion during deposition nitrogen-diamond like carbon coating on pure titanium.
- Author:
Lu YIN
1
;
Yun XIAO
Author Information
- Publication Type:Journal Article
- MeSH: Bacterial Adhesion; Carbon; Coated Materials, Biocompatible; Diamond; Humans; Nitrogen; Titanium
- From: West China Journal of Stomatology 2011;29(5):526-528
- CountryChina
- Language:Chinese
-
Abstract:
OBJECTIVEThe aim of this study was to observe the change of bacterial adhesion on pure titanium coated with nitrogen-diamond like carbon (N-DLC) films and to guide the clinical application.
METHODSN-DLC was deposited on titanium using ion plating machine, TiN film, anodic oxide film and non-deposition were used as control, then made specimens adhering on the surface of resin denture base for 6 months. The adhesion of Saccharomyces albicans on the titanium surface was observed using scanning electron microscope, and the roughness was tested by roughness detector.
RESULTSThe number of Saccharomyces albicans adhering on diamond-like carbon film was significantly less than on the other groups (P < 0.05), and the growth of bacterial cell was inhibited and in a poor state. The largest number of adhesion and cell strains grew well on anodic oxide film group and non-deposition control group. The change of surface roughness of N-DLC film was less than other group (P < 0.05).
CONCLUSIONPure titanium coated with N-DLC film reduced the adhesion of Saccharomyces albicans after clinical application, thereby reduced the risk of denture stomatitis.