Effect of metal conditioner on bonding of porcelain to cobalt-chromium alloy.
- Author:
Yoshito MINESAKI
1
;
Sadaaki MURAHARA
;
Yutaro KAJIHARA
;
Yoshihisa TAKENOUCHI
;
Takuo TANAKA
;
Shiro SUZUKI
;
Hiroyuki MINAMI
Author Information
- Publication Type:Original Article
- Keywords: Dental porcelain; Chromium alloys; Shear strength
- MeSH: Alloys*; Aluminum Oxide; Chromium Alloys; Dental Porcelain*; Fires; Shear Strength; Silicon
- From:The Journal of Advanced Prosthodontics 2016;8(1):1-8
- CountryRepublic of Korea
- Language:English
- Abstract: PURPOSE: The purpose of this study was to evaluate the efficacy of two different metal conditioners for non-precious metal alloys for the bonding of porcelain to a cobalt-chromium (Co-Cr) alloy. MATERIALS AND METHODS: Disk-shaped specimens (2.5x10.0 mm) were cast with Co-Cr alloy and used as adherend materials. The bonding surfaces were polished with a 600-grid silicon carbide paper and airborne-particle abraded using 110 microm alumina particles. Bonding specimens were fabricated by applying and firing either of the metal conditioners on the airborne-particle abraded surface, followed by firing porcelain into 5 mm in diameter and 3 mm in height. Specimens without metal conditioner were also fabricated. Shear bond strength for each group (n=8) were measured and compared (alpha=.05). Sectional view of bonding interface was observed by SEM. EDS analysis was performed to determine the chemical elements of metal conditioners and to determine the failure modes after shear test. RESULTS: There were significant differences among three groups, and two metal conditioner-applied groups showed significantly higher values compared to the non-metal conditioner group. The SEM observation of the sectional view at bonding interface revealed loose contact at porcelain-alloy surface for non-metal conditioner group, however, close contact at both alloy-metal conditioner and metal conditioner-porcelain interfaces for both metal conditioner-applied groups. All the specimens showed mixed failures. EDS analysis showed that one metal conditioner was Si-based material, and another was Ti-based material. Si-based metal conditioner showed higher bond strengths compared to the Ti-based metal conditioner, but exhibited more porous failure surface failure. CONCLUSION: Based on the results of this study, it can be stated that the application of metal conditioner is recommended for the bonding of porcelain to cobalt-chromium alloys.