Effect of Application of Tetracycline - HCl on Implant Surface - Scanning Electron Microscopic Study.
10.5051/jkape.2001.31.2.333
- Author:
Jung Ah HONG
1
;
Yeek HERR
;
Man Sup LEE
;
Joon Bong PARK
Author Information
1. Department of Periodontology, College of Dentistry, Kyung Hee University, Korea.
- Publication Type:Original Article
- MeSH:
Peri-Implantitis;
Tetracycline*;
Titanium
- From:The Journal of the Korean Academy of Periodontology
2001;31(2):333-344
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
The present study was performed to evaluate the effect of tetracycline - HCl on the change of implant surface microstructure according to application time. Implants with pure titanium machined surface and titanium plasma-sprayed surface were utilized. Implant surface was rubbed with 50mg/ml tetracycline - HCl solution for 1 min., 1 1/2 min., 2 min., 2 1/2 min. and 3min. respectively in the test group and with saline for 1 min. in the control group. Then, the specimens were processed for scanning electron microscopic observation. The following results were obtained. 1. Pure titanium machined surfaces conditioned with saline for 1 min., showed a few shallow grooves and ridges and were less irregular. 2. Pure titanium machined surfaces conditioned with 50mg/ml tetracycline - HCl solution showed more irregular and corrosive surfaces compared to the control group irrespective of the application time of tetracycline - HCl solution. 3. Titanium plasma-sprayed surfaces conditioned with saline for 1 min., were deposited with round or amorphous particles and showed round or irregular pores that can be connected to each other. 4. The irregularity of titanium plasma-sprayed surfaces conditioned with 50mg/ml tetracycline - HCl solution was lessened and the flattened areas were wider relative to the application time of tetracycline - HCl solution. 5. Titanium plasma-sprayed surfaces conditioned with tetracycline - HCl solution for 1 min. and 1 1/2 min. were very similar to that of the control group, but the surfaces conditioned for 2 min., 2 1/2 min. and 3 min. were changed. In conclusion, pure titanium machined surfaces were changed irrespective of the application time of tetracycline - HCl solution. And titanium plasma-sprayed surfaces conditioned with tetracycline - HCl solution began to be changed from 11/2 min. This results will be applicable to the regenerative procedures for peri-implantitis treatment.