A STUDY FOR SETTING AND THERMAL EXPANSION OF DENTAL SOLDERING INVESTMENTS.
- Author:
Sung Ae SHIN
;
Jang Seop LIM
;
Chang Mo JEONG
;
Young Chan JEON
- Publication Type:Original Article
- MeSH:
Dental Soldering*;
Heating;
Hot Temperature;
Investments*
- From:The Journal of Korean Academy of Prosthodontics
1999;37(6):730-740
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
The purpose of this study was to investigate setting and thermal expansion of dental soldering investments. In order to compare expansion rates and to investigate the effect of water/powder ratio on expansion, setting and thermal expansion of four dental soldering investments were measured under three different water/powder ratio conditions: standard, 20% decreased and 20% increased. Setting expansion of investments was measured by use of dialgauge method. Each measurement was started two minutes later from the beginning of spatulation and recorded every one minute for one hour. Thermal expansion of cylindrical test specimens, 10mm diameter, 50mm length, was recorded in a Thermodilatometer at heating rate of 10degrees C per minute from 25degrees C to 700degrees C. The results of this study were obtained as follows: 1. Setting expansion rates under the standard water/power ratio condition were 0.198% in Speed-E, 0.090% in Deguvest, 0.080% in CM and Hi-temp. Setting expansion of Speed-E was significantly different from those of CM, Deguvest and Hi-temp, and setting expansion of Deguvest was significantly different from those of CM and Hi-temp(p<.05). 2. Under the decreased water/powder ratio condition, there was significant increase in setting expansion of 4 dental soldering investments(p<.05). 3. There were no significant differences in setting expansions of investments except Hi-temp between standard and increased water/powder ratio condition(p<.05). 4. Thermal expansion rates under the standard water/powder ratio condition were 1.923% in Deguvest, 1.629% in Speed-E, 1.619% in Hi-temp and 1.580% in CM. No significant difference in thermal expansions under the standard water/powder ratio condition existed only between Speed-E and Hi-temp(p<.05). 5. Under the decreased water/powder ratio condition, there was significant increase in thermal expansion of CM and Deguvest but decrease in thermal expansion of Speed-E(p<.05). 6. Under the increased water/powder ratio condition, there was significant decrease in thermal expansion of CM, Deguvest and Speed-E but decrease in thermal expansion of Hi-temp(p<.05).