An in-vitro wear study of indirect composite resins against human enamel.
- Author:
Hyun Jeong YI
1
;
Young Chan JEON
;
Chang Mo JEONG
;
Hee Chan JEONG
Author Information
1. Department of Dentistry, College of Dentistry, Busan National University, Korea. jeonyc@paran.com
- Publication Type:Original Article
- Keywords:
Wear;
Indirect composite resin
- MeSH:
Alloys;
Bicuspid;
Cicatrix;
Composite Resins*;
Compressive Strength;
Dental Enamel*;
Humans*;
Hydrolysis;
Incisor;
Microscopy, Electron, Scanning;
Water
- From:The Journal of Korean Academy of Prosthodontics
2007;45(5):611-620
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
STATEMENT OF PROBLEM: Second-generation indirect composite resins have been improved flexural strength, compressive strength, hydrolytic degradation resistance, wear resistance compared to first-generation indirect composite resins, but there are still some problems as hydrolysis and low wear resistance. Some manufacturers claim that wear resistance of their materials has been improved, but little independent study has been published on wear properties of these materials and the properties specified in the advertising materials are largely derived from in-house or contracted testing. PURPOSE: This study was to evaluate the wear of indirect composite resins (SR Adoro, Sinfony, Tescera ATL) and gold alloy against the human enamel. MATERIAL AND METHOD: Extracted human incisors and premolars were sectioned to 2*2*2mm cube and embedded in the clear resin and formed conical shaped antagonist to fit the jig of pinon-disk tribometer. Total 20 antagonists were stored in distilled water. Five disk samples, 24mm in diameter and 1.5mm thick, were made for each of three groups of indirect composite resins and gold alloy group, and polished to #2,000 SiC paper on auto-polishing machine. Disk specimens were tested for wear against enamel antagonists. Wear test were conducted in distilled water using a pin-on-disk tribometer under condition (sliding speed 200rpm, contact load 24N, sliding distance 160m). The wear of the enamel was determined by weighing the enamel antagonist before and after test, and the weight was converted to volumes by average density. The wear tracks were analyzed by scanning electron microscopy and surface profilometer to elucidate the wear mechanisms. Statistical analysis of the enamel wear volume, wear track depth and wear tract width of disk specimens were accomplished with one-way ANOVA and the means were compared for significant differences with Scheffe's test. RESULTS: 1. The enamel wear was most in gold alloy, but there were no statistically significant differences among all the groups (P>.05). 2. In indirect composite resin groups, the group to make the most shallow depth of wear tract was Sinfony, followed by Tescera ATL, SR Adoro (P<.05). Gold alloy was shallower than Sinfony, but there was no statistically significant difference between Sinfony and gold alloy (P>.05). 3. The width of wear tract of SR Adoro was larger than the other groups (P<.05), and there were no statistically significant differences among the other groups (P>.05). 4. SEM analysis revealed that Sinfony and gold alloy showed less wear scars after test, Tescera ATL showed more wear scars and SR Adoro showed the most. CONCLUSION: Within the limits of this study, Sinfony and gold alloy showed the least wear rates and showed similar wear patterns.