AN EFFECT OF ND : YAG LASER ON THE BONDING STRENGTH OF COMPOSITE RESIN TO DENTIN AND PORCELAIN.
- Author:
Gum Jin WOO
1
;
Hong So YANG
Author Information
1. Dept. of Prosthodontics, Chonnam National University, Korea.
- Publication Type:Original Article
- MeSH:
Dental Porcelain*;
Dentin*;
Diamond;
Lasers, Solid-State*;
Water
- From:The Journal of Korean Academy of Prosthodontics
1997;35(2):385-400
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
The purpose of this experiment was to determine the effects of etching with a Nd : YAG Laser on dentin, or porcelain surface on the bond strength with composite resin. The dentin specimens were devided into the following 4 groups. D1 : No treatment D2 : Etched with 10% phosphoric acid D3 : Laser etched with 1W, 20PPs D4 : Laser etched with 2W, 20PPS The procelain specimens were devided into the following 4 groups. P1 : diamond roughened P2 : stched with HF acid P3 : Laser etched with 2W, 20PPS P4 : Laser etched with 3W, 20PPS All spedimens were veneered with resin. One half of the specimens were stored in 37degrees C water for one day and the other half were thermocycled 1000 times at temperature of 5degrees C to 55degrees C at 20 seconds intervals. After that, the bonding strength of composite resin to the dentin and porcelain was measured. The surface treated state and fractured state were observed with SEM. The following results were obtained. 1. In the dentin specimens, the bond strength of group D2 was higher than that of groups D1 and D3 in the case of the specimens stored in 37degrees C water for one day, there was a statistically significant difference between group D2 and D1,D3 (P<0.05). The bonding strength of the specimens that were thermocycled decreased in the following order : group D2,D4,D3 and then D1. 2. In the porcelain specimens, the bonding strength of groups P1,P2 were higher than that of group P3 in the case of the specimens stored in 37degrees C water for one day (P<0.05). The bonding strength of the specimens of being thermocycled decreased in the following order : group P2,P1,P4 and then P3. 3. The groups of high bond strength had a rougher surface and a high level of microporosity with SEM findings.