A STUDY ON THE EFFECT OF THERMOCYCLING TO THE PHYSICAL PROPERTIES OF DENTURE LINERS.
- Author:
Dong Su LEE
;
Heon Song LIM
;
Ju Hwan LIM
;
In Ho CHO
- Publication Type:Original Article
- MeSH:
Denture Liners*;
Dentures*;
Elasticity;
Mouth;
Tensile Strength;
Water
- From:The Journal of Korean Academy of Prosthodontics
2001;39(5):556-575
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
For the improvement of denture fitness of changed residual ridge, denture liner can be used. Denture liner should be very stable physically in various environments of the mouth as well as be bonded strongly with denture resin. In this study, the specimens bonded with four kinds of soft denture liner and three kinds of hard denture liner were used to test the physical properties of the liners. All experimental groups were stored in 37+/-1degrees C distilled water for 24hours, followed by thermocycling between 15degrees C and 45degrees C with 15 second dwell time. 1000, 2000, 3000 cycles of thermocycling were excuted and physical properties were measured by Instron Universal Testing Machine. The obtained results were as follows: 1. In tensile bond test of soft liners, it was shown that both of Molloplast-B(R) specimens before and after thermocycling had the highest tensile strength, and in case of hard liners, Dura-liner II(R)speimen had the highest tensile strength before and after thermocycling. Depending on thermocycling, Soft-Relining(R), Denture-Relining(R),Molloplast-B(R), Coe-soft(R) and Kooliner(R) specimen showed significant difference(p<0.05). 2. In strain test of soft liners, it was shown that Molloplast-B(R) specimen before thermocycling and the Coe-soft(R) after thermocycling showed highest results, and in case of hard liners, the Dura-Liner II(R) speimen before and after thermocycling had the highest result. Depending on thermocycling. Denture-Relinig(R). Molloplast-B(R) and Dura-Lner II(R) specimen showed significant difference(p<0.05). 3. In Maximum distance test of soft liners, the Molloplast-B(R) specimen before thermocycling and the Coe-soft(R) after thermocycling showed highest results, and in case of hard liners, the Dura-Liner II(R) specimen before and after thermocycling showed highest results. Depending on thermocycling, Denture-Relining(R), Molloplast-B(R) specimens showed significant difference(p<0.05). 4.In elasticity test of soft liners , the Molloplast-B(R) specimen before and after thermocycling showed highest results, and in case of hard liners, the Dura-Liner II(R) specimen before thermocycling and the Tokuso-Rebase (R) after thermocycling showed highest results. Depending on thermocycling, Soft-Relining(R) , Molloplast-B(R) specimens showed significant difference(p<0.05).