Evaluation on the abrasion resistance of a surface sealant.
10.5395/JKACD.2007.32.3.180
- Author:
Soo Mee KIM
1
;
Sae Hee HAN
;
Young Gon CHO
Author Information
1. Department of Dentistry, College of Medicine, Seonam University, Korea.
- Publication Type:Original Article
- Keywords:
Abrasion resistance;
Resin surface sealant;
Toothbrush abrasion test;
Surface roughness;
Finishing method;
Polishing instrument
- MeSH:
Head
- From:Journal of Korean Academy of Conservative Dentistry
2007;32(3):180-190
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
The purpose of this study was to evaluate the abrasion resistance of surface penetrating sealant which was applied on a composite resin restoration and to provide proper time to reapply sealant on composite resin surface. Two hundred rectangular specimens, sized 8 x 3 x 2 mm, were made of Micronew (Bisco, Inc., Schaumburg, IL, U.S.A) and divided into two groups; F group (n = 10) was finished with coarse and medium grit of Sof-Lex discs and BisCoverwas applied B group (n = 190) after finishing with discs. B group was again subdivided into nineteen subgroups. From B-1 group to B-18 group were subjected to toothbrush abrasion test using a distilled water-dentifrice slurry and toothbrush heads. B-IM group was not subjected to toothbrush abrasion test. Average surface roughness (Ra) of each group was calculated using a surface roughness tester (Surfcorder MSE-1700: Kosaka Laboratory Ltd., Tokyo, Japan). A representative specimen of each group was examined by FE-SEM (S-4700: Hitachi High Technologies Co., Tokyo, Japan). The data were analysed using cluster analysis, paired t-test, and repeated measure ANOVA. The results of this study were as follows; 1. Ra of F group was 0.898 +/- 0.145 microm and B-IM group was 0.289 +/- 0.142 microm. Ra became higher from B-1 group (0.299 +/- 0.48 microm) to B-18 group (0.642 +/- 0.313 microm). 2. Final cluster center of Ra was 0.361 microm in cluster 1 (B-IM ~ B-7), 0.511 microm in cluster 2 (B-8 ~ B-14) and 0.624 microm in cluster 3 (B-15 ~ B-18). There were significant difference among Ra of three clusters. 3. Ra of B-IM group was decreased 210.72% than Ra of F group. Ra of B-8 group and B-15 group was increased 35.49% and 51.35% respectively than Ra of B-IM group. 4. On FE-SEM, B-IM group showed the smoothest resin surface. B-8 group and B-15 group showed vertically shallow scratches, and wide and irregular vertical scratches on composite resin surface respectively. Within a limitation of this study, finished resin surface will be again smooth and glazy if BisCover would be reapplied within 8 to 14 months after applying to resin surface.