Histomorphometric study of machined titanium implants and calcium phosphate coated titanium implants.
10.4047/jkap.2010.48.2.122
- Author:
Hyun Joo KANG
1
;
Jae Ho YANG
Author Information
1. Department of Dentistry, School of Dentistry, Seoul National University, Seoul, Korea.
- Publication Type:Original Article
- Keywords:
Machined surface implant;
Calcium phosphate coated implant;
Electron-beam deposition;
Histomorphometry
- MeSH:
Calcium;
Calcium Phosphates;
Nitrogen Mustard Compounds;
Tibia;
Titanium
- From:The Journal of Korean Academy of Prosthodontics
2010;48(2):122-127
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
PURPOSE: The objective of this study was to investigate the effects of calcium phosphate coated titanium implant surface on bone response and implant stability at early stage of healing period of 3 weeks and later healing period of 6 weeks. MATERIAL AND METHODS: A total of 24 machined, screw-shaped implants (Dentium Co., Ltd., Seoul, Korea) which dimensions were 3.3 mm in diameter and 5.0 mm in length, were used in this research. All implants (n = 24), made of commercially pure (grade IV) titanium, were divided into 2 groups. Twelve implants (n = 12) were machined without any surface modification (control). The test implants (n = 12) were anodized and coated with thin film (150 nm) of calcium phosphate by electron-beam deposition. The implants were placed on the proximal surface of the rabbit tibiae. The bone to implant contact (BIC) ratios was evaluated after 3 and 6 weeks of implant insertion. RESULTS: The BIC percentage of calcium phosphate coated implants (70.8 +/- 18.9%) was significantly higher than that of machined implants (44.1 +/- 16.5%) 3 weeks after implant insertion (P = 0.0264). However, there was no significant difference between the groups after 6 weeks of healing (P > .05). CONCLUSION: The histomorphometric evaluation of implant surface revealed that: 1. After 3 weeks early healing period, bone to implant contact (BIC) percentage of calcium phosphate coated implants (70.8%) was much greater than that of surface untreated machined implants (44.1%) with P = 0.0264. 2. After 6 weeks healing period, however, BIC percentage of calcium phosphate coated implants group (79.0%) was similar to the machined only implant group (78.6%). There was no statistical difference between two groups (P = 0.8074). 3. We found the significant deference between the control group and experimental group during the early healing period of 3 weeks. But no statistical difference was found between two groups during the later of 6 weeks.