Desorption Kinetics and Structural Changes of Tetracycline Treated Barrier Membranes for Guided Tissue Regeneration.
10.5051/jkape.1997.27.1.1
- Author:
Sung Mi LEE
1
;
Hyun Ju CHUNG
Author Information
1. Department of Periodontology, College of Dentistry, Chonnam National University, Korea.
- Publication Type:Original Article
- MeSH:
Agar;
Bacillus cereus;
Ethanol;
Guided Tissue Regeneration*;
Hydrogen-Ion Concentration;
Immersion;
Kinetics*;
Membranes*;
Tetracycline*
- From:The Journal of the Korean Academy of Periodontology
1997;27(1):1-17
- CountryRepublic of Korea
- Language:Korean
-
Abstract:
Tetracycline is known to be effective in eliminating periodontopathogens and have collagenolytic activity. This study was performed to observe the desorption kinetics and structural changes of tetracycline-treated barrier membranes for guided tissue regeneration. Four kinds of barrier membranes were tested : Tefgen(R)(American Custom Medical, USA) and Gore-Tex(R)(W.L. Gore & Associates Inc., USA) as nonresorbable membranes ; Resolut(polyglycolide & polylactide copolymer, W.L. Gore & Associates Inc., USA) and Biomend(R)(collagen, Collatec Co., USA) as resorbable membranes. The membranes were cut into discs(diameter : 4mm) and were immersed in 5% tridodecylmethylammonium chloride(TIMAC) ethanol and air-dried. The membrane discs were absorbed with 100microgram/ml tetracycline solution(pH 8) for one minute and dried. For desorption kinetics, TC treated discs were immersed in phosphate buffered saline solution(PBS, pH 7.4). PBS was exchanged daily and TC concentration was measured by absorbance at 276nm on UV spectrophotometer. To measure remaining antibacterial activity, discs of 1 day to 4 weeks after desorption were placed on Mueller Hinton agar containing Bacillus cereus and incubated aerobically in 37degrees C for twelve hours and the inhibition diameters were measured. To observe the structural change of membranes after TIMAC treatment or immersion in PBS, the membrane discs were examined under SEM. The results were as follows : 1. Total amounts of TC absorbed into membrane discs(0.7536mm2) were 2000microgram, 1800microgram, 2625 microgram and 2499microgram for Tefgen(R), Gore-Tex(R), Biomend(R) and Resolut(R). 2. The concentration of TC released from barrier membrane discs was maintained over 4microgram/ml until the fifth day in nonresorbable membranes and Resolut(R), but until the fourth day in Biomend(R). Until the ninth day in nonresorbable membranes and until the seventh day in resorbable membranes, the TC concentration was maintained over 1microgram/ml. 3. The four membrane discs in the first day showed similar size of inhibition zone. One to four weeks later, the inhibition zone was much smaller in resorbable membrane discs than nonresorbable membrane discs. 4. Any structural change due to treatment of TIMAC was not observed on the nonresorbable membranes. Resolut(R) did not show any structural change except fibrillar loosening during immersion period, but Biomend showed destruction of membrane structure from the first week of immersion. This study indicates that tetracycline treated barrier membranes lead to the sustained release of tetracycline for over 7 days. This slow release pattern of tetracycline may contribute to the favorable clinical outcome of guided tissue regeneration.