Fabrication of a coral-like barium titanate nano-piezoelectric coating and its effect on promoting osteogenic differentiation of rat bone marrow mesenchymal stem cells in vitro
10.3760/cma.j.cn112144-20240307-00103
- VernacularTitle:珊瑚状钛酸钡纳米压电涂层促进大鼠骨髓间充质干细胞早期成骨分化的体外研究
- Author:
Luying LI
1
;
Ying LI
;
Meng LI
;
Wei ZHANG
;
Lingzhou ZHAO
;
Xiantong HU
;
Yantao ZHAO
;
Chufan MA
Author Information
1. 中国人民解放军空军特色医学中心口腔科，北京 100142
- Keywords:
Dental implants;
Nanotechnology;
Barium titanate;
Coating;
Low-intensity pulsed ultrasound;
Bone marrow mesenchymal stem cells;
Osteogenic differentiation
- From:
Chinese Journal of Stomatology
2024;59(6):578-585
- CountryChina
- Language:Chinese
-
Abstract:
Objective:To investigate the biocompatibility of coral-like barium titanate nano-piezoelectric coatings and the influence of ultrasound-excited piezoelectric effect on the early osteogenic differentiation.Methods:The barium titanate nano-piezoelectric coating (the coating group) was prepared on the surface of titanium metal by anodic oxidation, hydrothermal reaction and high-temperature annealing, and polished titanium specimens were used as control group. The surface morphology, composition, and crystal phase and hydrophilicity of the two groups of titanium specimens were characterized using scanning electron microscopy, X-ray photoelectron spectroscopy, Raman spectroscopy and contact angle meter. The piezoelectric properties of the materials were characterized by piezoresponse force microscopy. Rat bone marrow mesenchymal stem cells (BMSC) were cultured and identified and seeded the surface of titanium specimens in two groups. The cells seeded on blank culture plates were used as blank group. After low intensity pulsed ultrasound intervention, cell proliferation and live/dead staining were detected to evaluate cytocompatibility of the coatings. Alkaline phosphatase (ALP) activity of each group was detected by ALP staining kit, and the expression of osteogenesis-related genes [integrin, bone morphogenetic protein 2 (BMP-2), Runt-related transcription factor 2 (RUNX2)] was detected by real-time fluorescent quantitative PCR (RT-qPCR) to evaluate the effect of the coating on promoting the early osteogenic differentiation of BMSC.Results:The surface of titanium specimens in the coating group showed a uniform coral-like morphology, and the diameter of the coral tentacles was 70-100 nm. The main component was tetragonal barium titanate. The surface hydrophilicity of the coating group (water contact angle 10.12°± 0.93°) was significantly better than that of the control group (water contact angle 78.32°±0.71°) ( F= 10 165.91, P<0.001). The coating has a stable piezoelectric property with a piezoelectric constant of about 5 pC/N. Cell experiments showed that, with or without ultrasound, the cell proliferation activity of the coating group was significantly lower than that of the blank group and the control group on the third day ( P<0.05). On the fifth day, with or without ultrasound, there was no significant difference in cell proliferation activity between the three groups ( P>0.05). After 7 days of culture, the ALP activity of the coating group was significantly higher than that of the blank group and the control group ( P<0.05). The results of RT-qPCR showed that the mRNA expression of integrin and BMP-2 in the coating group with ultrasound was significantly higher than that in the other groups with ultrasound, and was higher than that of the coating group without ultrasound ( P<0.05). The expression of integrin mRNA in the control group with ultrasound was significantly higher than that in the control group without ultrasound ( P<0.05). The expression of RUNX2 mRNA in the coating group with ultrasound was significantly higher than that in the coating group without ultrasound ( P<0.05). Conclusions:The coral-like barium titanate nano-piezoelectric coating exhibits favorable biocompatibility and stable piezoelectric property, and facilitates the early osteogenic differentiation of BMSC under the excitation of low-intensity pulsed ultrasound.