Effect of chlorhexidine application on the bond strength of resin core to axial dentin in endodontic cavity.
10.5395/rde.2012.37.4.207
- Author:
Yun Hee KIM
1
;
Dong Hoon SHIN
Author Information
1. Department of Conservative Dentistry, Dankook University College of Dentistry and Institute of Dental Science, Cheonan, Korea. donyshin@dankook.ac.kr
- Publication Type:Original Article
- Keywords:
Chlorhexidine;
Endodontic cavity;
Microtensile bond strength;
Self-etch adhesive system;
Thermocycling;
Total-etch adhesive system
- MeSH:
Adhesives;
Bisphenol A-Glycidyl Methacrylate;
Chlorhexidine;
Composite Resins;
Dental Cements;
Dentin;
Molar;
Polymers
- From:Restorative Dentistry & Endodontics
2012;37(4):207-214
- CountryRepublic of Korea
- Language:English
-
Abstract:
OBJECTIVES: This study evaluated the influence of chlorhexidine (CHX) on the microtensile bonds strength (microTBS) of resin core with two adhesive systems to dentin in endodontic cavities. MATERIALS AND METHODS: Flat dentinal surfaces in 40 molar endodontic cavities were treated with self-etch adhesive system, Contax (DMG) and total-etch adhesive system, Adper Single Bond 2 (3M ESPE) after the following surface treatments: (1) Priming only (Contax), (2) CHX for 15 sec + rinsing + priming (Contax), (3) Etching with priming (Adper Single Bond 2), (4) Etching + CHX for 15 sec + rinsing + priming (Adper Single Bond 2). Resin composite build-ups were made with LuxaCore (DMG) using a bulk method and polymerized for 40 sec. For each condition, half of specimens were submitted to microTBS after 24 hr storage and half of them were submitted to thermocycling of 10,000 cycles between 5degrees C and 55degrees C before testing. The data were analyzed using ANOVA and independent t-test at a significance level of 95%. RESULTS: CHX pre-treatment did not affect the bond strength of specimens tested at the immediate testing period, regardless of dentin surface treatments. However, after 10,000 thermocycling, all groups showed reduced bond strength. The amount of reduction was greater in groups without CHX treatments than groups with CHX treatment. These characteristics were the same in both self-etch adhesive system and total-etch adhesive system. CONCLUSIONS: 2% CHX application for 15 sec proved to alleviate the decrease of bond strength of dentin bonding systems. No significant difference was shown in microTBS between total-etching system and self-etching system.