Preparation and characterization of methacryloylated hyaluronic acid/acellular Wharton's jelly composite hydrogel scaffold
- VernacularTitle:甲基丙烯酰化透明质酸/脱细胞华通胶水凝胶支架的制备与表征
- Author:
Xun YUAN
1
,
2
;
Zhengang DING
;
Liwei FU
;
Jiang WU
;
Yazhe ZHENG
;
Zhichao ZHANG
;
Guangzhao TIAN
;
Xiang SUI
;
Shuyun LIU
;
Quanyi GUO
Author Information
- Keywords: Wharton's jelly; methylacryloyl hyaluronic acid; hydrogel; scaffold; digital light processing 3D printing; cartilage injury; bone marrow mesenchymal stem cell; tissue engineering
- From: Chinese Journal of Tissue Engineering Research 2024;28(22):3517-3523
- CountryChina
- Language:Chinese
- Abstract: BACKGROUND:As tissue engineering brings new hope to the worldwide problem of articular cartilage repair,the construction of light-curing 3D printed hydrogel scaffolds with biomimetic composition is of great significance for cartilage tissue engineering. OBJECTIVE:To construct a biomimetic methacryloylated hyaluronic acid/acellular Wharton's jelly composite hydrogel scaffold by digital light processing 3D printing technology,and to evaluate its biocompatibility. METHODS:Wharton's jelly was isolated and extracted from human umbilical cord,then decellulated,freeze-dried,ground into powder,and dissolved in PBS to prepare 50 g/L acellular Wharton's jelly solution.Methylallylated hyaluronic acid was prepared,lyophilized and dissolved in PBS to prepare 50 g/L methylallylated hyaluronic acid solution.Acellular Wharton's jelly solution was mixed with methacrylyacylated hyaluronic acid solution at a volume ratio of 1:1,and was used as bio-ink after adding photoinitiator.Methylacrylylated hyaluronic acid hydrogel scaffolds(labeled as HAMA hydrogel scaffolds)and methylacrylylated hyaluronic acid/acellular Wharton's jelly gel scaffolds(labeled as HAMA/WJ hydrogel scaffolds)were prepared by digital light processing 3D printing technology,and the microstructure,swelling performance,biocompatibility,and cartilage differentiation performance of the scaffolds were characterized. RESULTS AND CONCLUSION:(1)Under scanning electron microscope,the two groups of scaffolds showed a three-dimensional network structure,and the fiber connection of HAMA/WJ hydrogel scaffold was more uniform.Both groups achieved swelling equilibrium within 10 hours,and the equilibrium swelling ratio of HAMA/WJ hydrogel scaffold was lower than that of HAMA hydrogel scaffold(P＜0.05).(2)CCK-8 assay showed that HAMA/WJ hydrogel scaffold could promote the proliferation of bone marrow mesenchymal stem cells compared with HAMA hydrogel scaffold.Dead/live staining showed that bone marrow mesenchymal stem cells grew well on the two groups of scaffolds,and the cells on the HAMA/WJ hydrogel scaffolds were evenly distributed and more cells were found.Phalloidine staining showed better adhesion and spread of bone marrow mesenchymal stem cells in HAMA/WJ hydrogel scaffold than in HAMA.(3)Bone marrow mesenchymal stem cells were inoculated into the two groups for chondrogenic induction culture.The results of qRT-PCR showed that the mRNA expressions of agglutinoglycan,SOX9 and type Ⅱ collagen in the HAMA/WJ hydrogel scaffold group were higher than those in the HAMA hydrogel scaffold group(P＜0.05,P＜0.01).(4)These findings indicate that the digital light processing 3D bioprinting HAMA/WJ hydrogel scaffold can promote the proliferation,adhesion,and chondrogenic differentiation of bone marrow mesenchymal stem cells.