In vitro cytological comparison of osseointegration properties between biomimetic bone trabecular and regular porous structure
- VernacularTitle:仿生骨小梁与规则多孔结构骨整合性能的体外细胞学对比研究
- Author:
Jiantao LIU
1
;
Zhiwei REN
1
;
Shuyuan ZHANG
2
;
Ruiyan WANG
2
;
Aofei XU
2
;
Xi GONG
2
;
Jia LI
1
;
Yingang ZHANG
1
Author Information
- Publication Type:Journal Article
- Keywords: biomimetic bone trabecular; regular porous structure; titanium alloy; osseointegration; implant
- From: Journal of Xi'an Jiaotong University(Medical Sciences) 2023;44(6):983-989
- CountryChina
- Language:Chinese
- Abstract: 【Objective】 To investigate the effects of biomimetic bone trabecular with the same porosity and pore size and regular porous structure on the adhesion, proliferation, and differentiation of osteoblasts, so as to provide theoretical basis for the improvement of osseointegration performance of titanium alloy implants. 【Methods】 The biomimetic bone trabecular and regular porous structures with the same porosity and pore size were generated by computer-aided software, and then processed into disc-shaped Ti6Al4V scaffolds with a diameter of 10 mm and a height of 3 mm by selective laser melting technology. MC3T3-E1 cells, the precursor cells of mouse osteoblasts in the logarithmic growth phase, were seeded on two kinds of scaffolds and divided into biomimetic bone trabecular group and regular porous structure group. After 3 hours of culture, acridine orange staining and phalloidin /DAPI staining were used to evaluate the number of cell adhesion. After 3 days of culture, the scaffolds were examined by scanning electron microscopy to evaluate the adhesion state of cells. After 1, 3, and 5 days of culture, the scaffolds were taken for CCK8 detection to observe the proliferation of cells. After 7 and 14 days of differentiation, alkaline phosphatase (ALP) activity was detected. After 14 days of differentiation, the expressions of osteogenesis-related genes (ALP, OCN, RUNX2) were detected by RT-PCR. After 30 days of differentiation, the scaffolds were stained with alizarin red and 100 g/L cetylpyridinium chloride was used to dissolve mineralized nodules. Calcium salt deposition was qualitatively and quantitatively detected to evaluate cell differentiation. 【Results】 The results of acridine orange and phalloidin /DAPI staining showed that the biomimetic trabecular Ti6Al4V scaffold adhered to more MC3T3-E1 cells than the regular porous structure, and the cytoskeleton of the former scaffold was more densely distributed. The results of scanning electron microscopy showed that the pseudopodia of MC3T3-E1 cells on the biomimetic bone trabecular Ti6Al4V scaffold were longer and the extension state was better than that of the regular porous structure. CCK8 test showed that the proliferation of MC3T3-E1 cells on the biomimetic trabecular bone titanium alloy scaffold was significantly higher than that on the regular porous structure on the 3rd and 5th day, and the difference gradually increased with the increase of time, with statistical significance (P<0.05). The results of cell differentiation test showed that ALP activity on the bionic trabecular scaffold was higher than that on the regular porous structure (P<0.05). The expressions of osteogenic genes (ALP, OCN, RUNX2) in MC3T3-E1 cells on the biomimetic bone trabecular titanium alloy scaffold were significantly higher than those on the regular porous structure (P<0.05). After 30 days of induction, the amount of calcium salt deposited in the bionic trabecular titanium alloy scaffold was significantly larger than that in the regular porous structure (P<0.05). 【Conclusion】 The biomimetic bone trabecular with a porosity of 65% and an equivalent pore size of 600 μm is more conducive to the adhesion, proliferation and differentiation of mouse osteoblast precursor cells MC3T3-E1 on the titanium alloy scaffold than the regular porous structure with the same porosity and pore size. It is theoretically more conducive to improving the osseointegration performance of titanium alloy implants.