OBJECTIVES: The current study aimed to investigate the bonding properties of a novel low-shrinkage resin adhesive containing expanding monomer and epoxy resin monomer after thermal cycling aging treatment. METHODS: Expanding monomer of 3,9-diethyl-3,9-dimethylol-1,5,7,11-tetraoxaspiro-[5,5] undecane (DDTU) as an anti-shrinkage additive and unsaturated epoxy monomer of diallyl bisphenol A diglycidyl ether (DBDE) as a coupling agent were synthesized. A blend of DDTU and DBDE at a mass ratio of 1∶1, referred to as "UE", was added into the resin matrix at the mass fraction of 20% to prepare a novel low-shrinkage resin adhesive.Then, the methacrylate resin adhesive without UE was used as the blank control group, and a commercial resin adhesive system was selected as the commercial control group. Moreover, the resin-dentin bonding and micro-leakage testing specimens were prepared for the thermal cycling aging treatment. The bonding strength was tested, the fracture modes were calculated, the bonding fracture surface was observed by scanning electron microscope (SEM), and the dye penetration was used to evaluate the tooth-restoration marginal interface micro-leakage. All the data were analyzed statistically. RESULTS: After aging, the dentin bonding strength of the experimental group was (19.20±1.03) MPa without a significant decrease (P>0.05), that of the blank control group was (11.22±1.48) MPa with a significant decrease (P<0.05) and that of the commercial control group was (19.16±1.68) MPa without a significant decrease (P>0.05). The interface fracture was observed as the main fracture mode in each group after thermal cycling by SEM. The fractured bonding surfaces of the experimental group often occurred on the top of the hybrid layer, whereas those of the blank and commercial control groups mostly occurred on the bottom of the hybrid layer. Micro-leakage rating counts of specimens before and after thermal cycling were as follows: the experimental group was primarily 0 grade, thereby indicating that a relatively ideal marginal sealing effect could be achieved (P>0.05); meanwhile, the blank control group was primarily 1 grade, and the penetration depth of dye significantly increased after thermal cycling (P<0.05); the commercial control group was primarily 0 grade without statistical difference before and after thermal cycling (P>0.05), while a significant difference was observed between the commercial control group and experimental group after thermal cycling (P<0.05). CONCLUSIONS The novel low-shrinkage resin adhesive containing 20%UE exhibited excellent bonding properties even after thermal cycling aging treatment, thereby showing a promising prospect for dental application.
Composite Resins ; Dental Bonding ; Dental Cements ; Surface Properties ; Resin Cements ; Dentin-Bonding Agents ; Dentin ; Materials Testing ; Microscopy, Electron, Scanning

The existing dentin bonding systems based on acid-etching technique lead to the loss of both extrafibrillar and intrafibrillar minerals from dentin collagen, causing excessive demineralization. Because resin monomers can not infiltrate the intrafibrillar spaces of demineralized collagen matrix, degradation of exposed collagen and resin hydrolysis subsequently occur within the hybrid layer, which seriously jeopardizing the longevity of resin-dentin bonding. Collagen extrafibrillar demineralization can effectively avoid the structural defects within the resin-dentin interface caused by acid-etching technique and improve the durability of resin-dentin bonding, by preserving intrafibrillar minerals and selectively demineralizing extrafibrillar dentin. The mechanism and research progress of collagen extrafibrillar demineralization in dentin bonding are reviewed in the paper.
Humans ; Collagen ; Dental Bonding ; Dentin/chemistry* ; Dentin-Bonding Agents/chemistry* ; Materials Testing ; Minerals ; Resin Cements/chemistry* ; Tooth Demineralization

OBJECTIVES: Root canal therapy is the most effective and common method for pulpitis and periapical periodontitis. During the root canal preparation, chemical irrigation plays a key role. However, sodium hypochlorite (NaOCl), the widely used irrigation fluid, may impact the bonding strength between dentin and restorative material meanwhile sterilization and dissolving. Therefore, it's important to explore the influence of NaOCl on the adhesion between dentin and restoration materials to ensure clinical efficacy. This study aims to explore the effect of NaOCl on dentine adhesion and evaluate the effect of dentine adhesion induced by sodium erythorbate (ERY), and to provide clinical guidance on dentin bonding after root canal therapy. METHODS: Seventy freshly complete extracted human third molars aged 18-33 years old, without caries and restorations were selected. A diamond saw was used under running water to achieve dentine fragments which were divided into 10 groups with 14 fragments in each group: 2 control [deionized water (DW)±10% ERY] and 8 experimental groups (0.5%, 1%, 2.5%, and 5.25% NaOCl±10% ERY). The dentine specimens in the control group (treated with DW) and the experimental groups (treated with 0.5% NaOCl, 1% NaOCl, 2.5% NaOCl, and 5.25% NaOCl) were immersed for 20 min using corresponding solutions which were renewed every 5 min. The other 5 groups were immersed in 10% ERY for 5 min after an initial washing with DW for 1 min. Then, we selected 4 dentine fragments from all 14 fragments in each group and the numbers and diameters of opening dentinal tubules were observed under scanning electron microscope (SEM). The other 10 dentine fragments from each group were used to make adhesive samples by using self-etch adhesive wand composite resin. All the above adhesive samples were sectioned perpendicular to the bonded interface into 20 slabs with a cross-sectional area of 1 mm×1 mm using a diamond saw under the cooling water, and then the morphology of 10 slabs in each group's bonding interface was observed from aspects of formation of resin tags, depth of tags in dentin, and formation of hybrid layer under SEM. The other 10 slabs of each group's microtensile bond strength and failure modes were also analyzed. RESULTS: Among the 0.5% NaOCl, 1% NaOCl, 2.5% NaOCl, and 5.25% NaOCl groups, the number and diameter of patent dentinal tubules gradually increased with the rise of concentration of NaOCl solution (all P<0.05). Among the DW, 0.5% NaOCl, 1% NaOCl, 2.5% NaOCl, and 5.25% NaOCl groups, the number and diameter of patent dentinal tubules increased after using ERY, but without significant difference (all P>0.05). Among the DW, 0.5% NaOCl, 1% NaOCl, and 2.5% NaOCl groups, the scores of formation of resin tags under SEM gradually increased with the increase of concentration of NaOCl solution, while the score in the 5.25% NaOCl group decreased significantly compared with the score of the 2.5% NaOCl group (P<0.05). There was no significant difference between using 10% ERY groups and without using 10% ERY groups (all P>0.05). The scores of length of the tags under SEM in the 5.25% NaOCl group was significantly higher than the scores of DW, 0.5% NaOCl, and 1% NaOCl groups (all P<0.05), and it was also higher than the score of the 2.5% NaOCl group, but without significant difference (P>0.05). There was no significant difference between using 10% ERY groups and without using 10% ERY groups (P>0.05). The scores of formation of hybrid layer under SEM in the 2.5% NaOCl and 5.25% NaOCl groups significantly decreased compared with the score of the DW group (all P<0.05). There were significant differences between the 2.5% NaOCl±10% ERY groups and between the 5.25% NaOCl±10% ERY groups (all P<0.05). Microtensile bond strength was greater in the 0.5% NaOCl, 1% NaOCl, and 2.5% NaOCl groups, but lower in the 5.25% NaOCl group than that in the DW group (all P<0.05). There were significant differences between the 2.5% NaOCl±10% ERY groups and between the 5.25% NaOCl±10% ERY groups (all P<0.05). The incidence of type "Adhesive" of failure modes in the 5.25% NaOCl group was significantly higher than that in other groups (all P<0.05), while the incidence of type "Adhesive" in the 5.25% NaOCl+10% ERY group was lower than that in the 5.25% NaOCl group (P<0.05). CONCLUSIONS The bonding strength to dentine increases with the increase of NaOCl concentration when the concentration lower than 2.5%; whereas it is decreased at a higher concentration (such as 5.25%). 10% ERY has a definite recovery effect on attenuated bonding strength to 5.25% NaOCl-treated dentine.
Adolescent ; Adult ; Ascorbic Acid ; Dental Bonding ; Dentin ; Dentin-Bonding Agents/pharmacology* ; Diamond/pharmacology* ; Humans ; Materials Testing ; Microscopy, Electron, Scanning ; Resin Cements/pharmacology* ; Sodium Hypochlorite/pharmacology* ; Tensile Strength ; Water/pharmacology* ; Young Adult

As a convenient and effective surface modification approach, non-thermal atmospheric pressure plasma (NTAPP)can be used to improve dentin bonding, and has recently become a research focus. Studies have shown that NTAPP can alter dentin surface properties, improve the penetration and polymerization of adhesives, stimulate the cross-linking of collagen, and change the micro-morphology and element content of dentin surface, thus improve the dentin bonding quality. This article introduces the current research progress in the application of NTAPP in the field of dentin bonding, in order to provide innovative information for future research in optimization of the quality of dentin bonding.
Dental Bonding ; Dental Cements ; Dentin ; Dentin-Bonding Agents ; Materials Testing ; Plasma Gases ; Resin Cements ; Surface Properties

Objective: To evaluate the effect of shear bond strength between resin cement and zirconia using SiO₂-ZrO₂ slurry coating. Methods: One hundred and forty pre-sintered zirconia discs were randomly divided into seven groups (n=20) according to the surface treatments: AS (as-sintered), SB (sand blasting with Al₂O₃), 2SiO₂-1ZrO₂ (2∶1 mole ratio SiO₂-ZrO₂ coating), 1SiO₂-1ZrO₂ (mole ratio 1∶1 SiO₂-ZrO₂ coating), 1SiO₂-2ZrO₂ (mole ratio 1∶2 SiO₂-ZrO₂ coating), 1SiO₂-3ZrO₂ (mole ratio 1∶3 SiO₂-ZrO₂ coating), 1SiO₂-4ZrO₂ (mole ratio 1∶4 SiO₂-ZrO₂ coating). Each zirconia disc was bonded to composite resin cylinder using resin cement. All specimens were stored in distilled water (37 ℃, 24 h). Each group was divided into two subgroups in which half specimens were tested using universal testing machine and another half specimens accepted artificial aging of 5 000 times thermocycling then tested. Scaning electron microscopy (SEM) was used to observe the micro-morphology of coating surface etched by hydrofluoric acid,then the coating thickness was measured. Results: Before artificial aging, 1SiO₂-1ZrO₂ showed a higher shear bond strength [(41.69±6.28) MPa] than all the other group (P<0.05). 1SiO₂-2ZrO₂ gained a higher strength than AS, SB, 1SiO₂-3ZrO₂ and 1SiO₂-4ZrO₂ (P<0.05). However, 1SiO₂-2ZrO₂ did not get a significant higher shear bond strength than 2SiO₂-1ZrO₂ (P>0.05). No significant differences were found among SB, 2SiO₂-1ZrO₂ and 1SiO₂-3ZrO₂ (P>0.05). After artificial aging, shear bond strength of all groups were decreased significantly besides 2SiO₂-1ZrO₂. 2SiO₂-1ZrO₂, 1SiO₂-1ZrO₂ and 1SiO₂-2ZrO₂ [(24.13±5.50), (22.28±4.40), (23.11±4.80) MPa] showed higher shear bond strength than SB and 1SiO₂-3ZrO₂ (P<0.05),no intergroup differences were observed (P>0.05). Shear bond strength of AS and 1SiO₂-4ZrO₂ fell to 0 MPa approximately. The SEM images of etched coating surface showed contraction fissure due to different thermal expansion coefficient between SiO₂ and ZrO₂ and intercrystal pores of zirconia. The thickness of coating was measured to be less than 30 μm. Conclusions: Mole ratio 1∶1 SiO₂-1ZrO₂ slurry coating showed the highest shear bond strength of resin cement to zirconia.
Dental Bonding ; Materials Testing ; Resin Cements/chemistry* ; Silicon Dioxide ; Surface Properties ; Zirconium

Objective: To study the effect of hydroxyapatite (HA) based agents on the bonding properties of universal adhesive with different application modes, and to provide evidence for the use of adhesives after desensitization treatment. Methods: Sixty impacted third molars were extracted and selected (acquired from Department of Oral and Maxillofacial Surgery, College of Stomatology, Xi'an Jiaotong University). Four third molars were used to prepare 1 mm thick dentin disks and treated with 1% citric acid to simulate sensitive tooth models. The dentin surfaces were observed by scanning electron microscope (SEM) after treating with no desensitization (control group), desensitized by HA based toothpaste Biorepair and Dontodent Sensitive respectively (desensitizing toothpaste A group and B group), or HA paste treatment (desensitizing paste group ) (n=2 per group). The remaining teeth were selected to expose the mid-coronal dentin and establish dentin sensitivity models. Then, the specimens were divided into 4 former groups and received corresponding treatment. Each group was randomly divided into 2 subgroups, and intermediately strong universal adhesive (G-Premio Bond) was applied on the desensitized dentin by either etch-and-rinse mode or self-etch mode. Resin-dentin slice specimens (n=4 per subgroup), microtensile specimens (n=20 per subgroup) and slice specimens (n=6 per subgroup) were prepared. The microstructure and nanoleakage of the adhesive interfaces were observed by scanning electron microscopy (SEM). The microtensile strength (bond strength) and fracture mode were tested and recorded. The water permeability of the adhesive interface was observed by laser scanning confocal microscopy (LSCM). Results: SEM showed that desensitizing toothpaste and desensitizing paste could partially or entirely occlude most of the dentin tubules. For the etch-and-rinse mode, the bond strength of specimens treated with toothpaste A [(40.98±4.60) MPa], toothpaste B [(40.89±4.64) MPa] and HA paste [(41.48±3.65) MPa] was significantly higher than that of the control group [(38.58±4.28) MPa] (F=3.89,P<0.05). There was no statistically significant difference in bond strength among the 4 subgroups for self-etch modes (F=0.48,P>0.05). After desensitization, the bond strength of the control group and desensitizing groups in the self-etch mode was significantly higher than that in the etch-and-rinse mode (P<0.05). The overall fracture modes were mixed failure and interfacial failure in the control group and desensitizing groups. SEM showed speckled silver-stained particles deposited along the bottom of the hybrid layer on the bond interface of etch-and-rinse mode, and there were few silver-stained particles deposited on the bond interface of self-etch mode. LSCM showed continuous linear penetration in the hybrid layer of etch-and-rinse mode subgroups and discontinuous linear penetration in the hybrid layer of self-etch mode subgroups. Conclusions: HA based desensitizers have no adverse effect on the bond strength of intermediately strong universal adhesive and show good bonding performance accompanied with the self-etch mode.
Adhesives ; Dental Bonding ; Dental Cements ; Dentin ; Dentin-Bonding Agents ; Durapatite ; Humans ; Materials Testing ; Microscopy, Electron, Scanning ; Resin Cements ; Tensile Strength

OBJECTIVES: This study aimed to evaluate the color stability of tetracycline teeth restored with ceramic veneers of different thicknesses combined with different resin cement systems after aging. METHODS: Twenty patients with tetracycline teeth, including two maxillary central incisors, were selected clinically. The patients were randomly divided into four groups and restored with 0.5 and 0.75 mm ceramic veneers by using a veneer adhesive system, either with light-cured or dual-cured reaction. The color difference (ΔE) values after cementation and 1, 6, 12, and 24 months of use were obtained by quantification of L*, a*, and b* values with a colorimeter. The results were analyzed statistically with two-way ANOVA and Student's RESULTS: The ΔE values of ceramic veneers detected after aging were less than 2.25. The 0.5 mm groups exhibited greater color change than the 0.75 mm-thick veneers ( CONCLUSIONS Resin cements and veneer thickness influence the color of ceramic veneers after aging. Cementation of veneers with either dual- or light-cured resin cements does not affect the long-term color stability of tetracycline teeth differently.
Ceramics ; Color ; Dental Porcelain ; Dental Veneers ; Humans ; Materials Testing ; Resin Cements ; Tetracyclines

To investigate the effect of captopril on the dentin bonding durability of self-etch adhesive. Different concentrations of captopril ethanol solutions or captopril ethanol/water solutions were prepared to pretreat dentin as primer for the self-etch adhesives. The surface morphology of the dentin was observed with scanning electron microscopy (SEM). Based on the morphology analysis, the pretreatment condition was selected and two self-etch adhesives were employed to evaluate the improvement effect of the captopril pretreatment on the dentin bonding durability. : SEM showed that the pretreatment of captopril ethanol solutions and captopril ethanol/water solutions were able to remove the smear lay and partially expose collagen matrix. According to the SEM results, the pretreating condition of captopril ethanol/water solution with the pretreating time of was selected for further dentin bonding study. For Clearfil SEBOND system, the immediate bonding strength increased from to  (<0.05). After one-year aging, the bonding strength of the control group decreased markedly [(22.90±6.82) MPa, <0.05]; while the bonding strength of the captopril pretreated group kept steadily >0.05]. For Clearfil S BOND system, there was no significant difference in the immediate bonding strength between the experimental group [(4.07) MPa] and the control group[(4.11) MPa]. But after one-year aging, the bonding strength of the experimental group was higher than that of the control group <0.05]. : The pretreatment with captopril ethanol/water solution increases the dentin bonding strength of the self-etch adhesive systems and also improves the bonding durability.
Adhesives ; Captopril ; Dental Bonding ; Dentin ; Dentin-Bonding Agents ; Materials Testing ; Microscopy, Electron, Scanning ; Resin Cements

Fiber-reinforced resin composite posts (fiber posts) are used extensively for the restoration of root-treated teeth with excessive loss of coronal structure. However, the longevity of a fiber post restoration still needs to be improved because of the various confounding factors that affect bonding procedures. Operational specification for clinical use of dental intraradicular fiber post was established based on the in-depth discussions by a panel of experts from Society of Prosthodontics, Chinese Stomatological Association. This specification should be helpful in standardizing the clinical technique of fiber post placement and improving the clinical longevity of a fiber post restoration.
Cementation ; Composite Resins ; Dental Bonding ; Dental Stress Analysis ; Glass ; Materials Testing ; Post and Core Technique ; Resin Cements ; Tooth Root

OBJECTIVES: This study investigated the effects of a hydrofluoric acid (HA; solution of hydrogen fluoride [HF] in water)-based smart etching (SE) solution at an elevated temperature on yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) ceramics in terms of bond strength and morphological changes.MATERIALS AND METHODS: Eighty sintered Y-TZP specimens were prepared for shear bond strength (SBS) testing. The bonding surface of the Y-TZP specimens was treated with 37% phosphoric acid etching at 20°C–25°C, 4% HA etching at 20°C–25°C, or HA-based SE at 70°C–80°C. In all groups, zirconia primers were applied to the bonding surface of Y-TZP. For each group, 2 types of resin cement (with or without methacryloyloxydecyl dihydrogen phosphate [MDP]) were used. SBS testing was performed. Topographic changes of the etched Y-TZP surface were analyzed using scanning electron microscopy and atomic force microscopy. The results were analyzed and compared using 2-way analysis of variance.RESULTS: Regardless of the type of resin cement, the highest bond strength was measured in the SE group, with significant differences compared to the other groups (p < 0.05). In all groups, MDP-containing resin cement yielded significantly higher bond strength values than MDP-free resin cement (p < 0.05). It was also shown that the Y-TZP surface was etched by the SE solution, causing a large change in the surface topography.CONCLUSIONS: Bond strength significantly improved when a heated HA-based SE solution was applied to the Y-TZP surface, and the etched Y-TZP surface was more irregular and had higher surface roughness.
Ceramics ; Hot Temperature ; Hydrofluoric Acid ; Microscopy, Atomic Force ; Microscopy, Electron, Scanning ; Resin Cements