Histocompatibility of noval xenogenic tendon matrix materials
10.3760/cma.j.issn.1671-0290.2012.06.015
- VernacularTitle:异种肌腱基质填充材料的组织相容性
- Author:
Xueying XIA
;
Ping JIANG
;
Wei ZHANG
;
Guofeng XU
;
Nengyu ZHAO
;
Shenghan ZHAI
;
Yong MIAO
- Publication Type:Journal Article
- Keywords:
Xenogenic tendon matrix;
Histocompatibility;
Silicon
- From:Chinese Journal of Medical Aesthetics and Cosmetology
2012;(6):447-449
- CountryChina
- Language:Chinese
-
Abstract:
Objective To evaluate the histocompatibility of novel manufactured xenogenic tendon matrix materials by an animal experimental study.Methods The study was conducted on 15 dogs,weighing 10-13 kg.The prepared xenogenic tendon matrix materials were implanted into the bilateral area of spine in dogs subcutaneously (experimental group),and the implantation of silicon served as control group.The animals were killed 14,30,60 days after surgery and the specimens were processed in laboratory to receive gross and histology observation.The histological sections were stained with hematoxylin-eosin and analyzed by light microscopy.Scores were assigned to the inflammatory process and statistically compared by two related samples with non-parametric test.Results All dogs survived well during the embedded test.There was no tissue necrosis,effusion or inflammation at all implantation sites in both groups during the test.The xenogenic implant materials promoted slight to moderate inflammation process after 14 days,with no statistically significant difference compared to the control.However,after 30 days,there was a regression of inflammation.After 60 days,it was observed the presence of well-organized connective tissue,and few inflammatory cells.Score evaluation of inflammation response at different time after operation of two groups showed no statistically significant difference (P＞0.05).Conclusions The new xenogenic tendon matrix materials are considered biocompatible with subcutaneous tissue.